Simultaneously enhancing mechanical and microwave absorption properties of Cf/SiC composites via SiC nanowires additions

C_f/SiC composite is an excellent structural and functional material, silicon carbide nanowires (SiCnws) are not only a toughening material but also a great application in the field of microwave absorption. In this study, SiCnws are grown on the surface of carbon fiber (C_f) by polymer impregnation and pyrolysis, and the SiC matrix was prepared by chemical vapor osmosis method. The SiCnws are introduced to enhance the mechanical and microwave absorption properties simultaneously. After 3 impregnations, the flexural strength of the composite was 107.35 ± 10 MPa. When the thickness is 1.86 mm, the minimum reflection loss value is ?41.08 dB, and the effective absorption bandwidth (RL ≤ ?10 dB) is 3.86 GHz. Furthermore, the microwave absorption mechanism of the material is discussed. This work provides a new method to prepare lightweight, stable and high-performance microwave absorption materials, and these materials are expected to be used in high temperature environments.     

Efficient dye-sensitized solar cells based on CNTs and Zr-doped TiO2 nanoparticles

The light scattering, harvesting and adsorption effects in dye-sensitized solar cells (DSSCs) are studied by preparation of coated carbon nanotubes (CNTs) with TiO₂ and Zr-doped TiO₂ nanoparticles in the forms of mono- and double-layer cells. X-ray diffraction (XRD) analysis reveals that the phase composition of Zr-doped TiO₂ electrode is a mixture of anatase and rutile phases with major rutile content, whereas it is the same mixture with major anatase content for coated CNTs with TiO₂. Furthermore, the average crystallite size of Zr-doped TiO₂ electrode is slightly decreased with Zr introduction. Field emission scanning electron microscope (FE-SEM) images show that the porosity of Zr-doped TiO₂ electrodes is higher than that of undoped electrode, enhancing dye adsorption. UV–visible spectroscopy analysis reveals that the absorption onset of Zr-doped TiO₂ electrodes is slightly shifted to longer wavelength (the red-shift) in comparison with that of undoped TiO₂ electrode. Moreover, the band gap energy of TiO₂ nanoparticles is decreased by Zr introduction, enhancing light absorption. It is found that electron injection of monolayer TiO₂ electrode is improved by introduction of 0.025 mol% Zr, resulted in enhancement of its power conversion efficiency (PCE) up to 6.81% compared with 6.17% for pure TiO₂ electrode. Moreover, electron transport and light scattering are enhanced by incorporation of 0.025 wt% coated CNTs with TiO₂ in the over-layer of double layer electrode. Therefore, double layer solar cell composed of 0.025 mol% Zr-doped TiO₂ nanoparticles as the under-layer and mixtures of these nanoparticles and 0.025 wt% coated CNTs with TiO₂ as the over-layer shows the highest PCE of 8.19%.     

The significant promotion of g-C3N4 on Pt/CNS catalyst for the electrocatalytic oxidation of methanol

This article reported a series of g–C₃N₄–CNS (g-C₃N₄ and carbon nanosheets) composite carriers formed by the hydrothermal method, and then the ethylene glycol reduction method was used to anchor Pt nanoparticles on the g–C₃N₄–CNS carrier to form the Pt/g–C₃N₄–CNS catalysts. The electrochemical test for the electrocatalytic oxidation of methanol (MOR) shown that the Pt/20%g–C₃N₄–CNS catalyst has the best catalytic performance and stability. These Pt/g–C₃N₄–CNS catalysts were analyzed by TEM, XRD, XPS, and BET characterization. It is discovered that the amount of g-C₃N₄ greatly influenced the structure and chemical properties of Pt/CNS precursor. As the content of g-C₃N₄ increases, the content of pyridine nitrogen and pyrrole nitrogen also increases, and N species can enhance the interaction between Pt nanoparticles and CNS, promote Pt dispersion, and increase the specific surface area of the catalyst. Similarly, an excessive addition of g-C₃N₄ will cause a sharp decline in the conductivity of the catalyst, and then led to the decline of MOR activity.     

Experimental study to assess the effect of carbon nanotube addition on the through-thickness electrical conductivity of CFRP laminates for aircraft applications

The present paper tests experimentally the through-thickness electrical conductivity of carbon fiber-reinforced polymer (CFRP) composites laminates for aircraft applications. Two types of samples were prepared: Type A samples with carbon nanotubes (CNTs) and Type B samples without CNTs. During the electrical experiments, electrical currents of several mA were injected through the specimens. Electrical resistance was monitored simultaneously in order to deduce the changes in the through-the-thickness electrical conductivity caused by the addition of CNTs. Improvement of electrical conduction by two orders of magnitude was achieved through the addition of 1 wt% carbon nanotubes as compared to classic CFRP without CNTs. For moisture saturated samples, the influence of moisture absorption on such measures was found to be negligible.     

Tough salami-inspired Cf/ZrB2 UHTCMCs produced by electrophoretic deposition

One of the biggest challenges of the materials science is the mutual exclusion of strength and toughness. This issue was minimized by mimicking the natural structural materials. To date, few efforts were done regarding materials that should be used in harsh environments. In this work we present novel continuous carbon fiber reinforced ultra-high-temperature ceramic matrix composites (UHTCMCs) for aerospace featuring optimized fiber/matrix interfaces and fibers distribution. The microstructures – produced by electrophoretic deposition of ZrB₂ on unidirectional carbon fibers followed by ZrB₂ infiltration and hot pressing – show a maximum flexural strength and fracture toughness of 330 MPa and 14 MPa m^1/2, respectively. Fracture surfaces are investigated to understand the mechanisms that affect strength and toughness. The EPD technique allows the achievement of a peculiar salami-inspired architecture alternating strong and weak interfaces.     

New anti-ablation candidate for carbon/carbon composites: Preparation,composition and ablation behavior of Y2Hf2O7 coating under an oxyacetylene torch

Y₂Hf₂O₇ possesses low thermal conductivity and high melting point, which make it promising for a new anti-ablation material. For evaluating the thermal stability and the potential applications of Y₂Hf₂O₇ on anti-ablation protection of C/C composites, Y₂Hf₂O₇ ceramic powder was synthesized by solution combustion method and Y₂Hf₂O₇ coating was prepared on the surface of SiC coated C/C composites using SAPS. Results shown that the coating exhibits good ablation resistance under the heat flux of 2.4?MW/m² with the linear and mass ablation rates are 0.16?μm?s^?1 and ?0.028?mg?s^?1, respectively, after ablation for 40?s. With the prolonging of the ablation time, the increasing thermal stress causes the increase of cracks. Moreover, the chemical erosion from SiO₂ and the physical volatilization of low temperature molten products aggravate failure of the Y₂Hf₂O₇ coating.     

Effects of short carbon fiber on the macro-properties,mechanical performance and microstructure of SiSiC composite fabricated by selective laser sintering

Selective laser sintering was combined with reactive melt infiltration to fabricate SiSiC part, and the effects of carbon fiber (C_f) on the properties of the SLS green body, the carbonized and final SiSiC sample were investigated. Results show that the addition of an appropriate amount of C_f (1.59 wt%~2.97 wt%) can increase the bulk density and geometric precision of the sample at all stages, and improve the mechanical properties of green and carbonized samples. The main phases composed of the SiSiC composite were free Si, a-SiC, β-SiC, plus a very small amount of Al–Si alloy. With 1.59 wt% C_f addition, a relatively comprehensive favorable macro-properties of both the green sample and carbonized sample was achieved, and the homogeneous microstructure of the latter favored the decreased free Si content and increased β-SiC content of the final composite. The evolution mechanism of C_f added to the raw material is inferred to be the mutual diffusion of [C] and [Si] that occurred at the C_f/Si melt boundary leading to the formation of the siliconized C_f with relatively large diameter size (24.3 μm) and high aspect ratio (>30). Amorphous C, which derived from the pyrolysis of epoxy resin E12, undergone a dissolution-precipitation mechanism with the formation of fine-grain β-SiC.     

Neutral axis depth and moment redistribution in FRP and steel reinforced concrete continuous beams

The neutral axis depth is considered the best parameter for quantifying the moment redistribution in continuous concrete beams, as exemplified in various design codes worldwide. It is therefore important to well understand the variation of neutral axis depth against moment redistribution. This paper describes a theoretical investigation into the neutral axis depth and moment redistribution in concrete beams reinforced with fibre reinforced polymer (FRP) and steel bars. A finite element model has been developed. The model predictions are in favourable agreement with experimental results. Three types of reinforcement are considered, namely, glass fibre, carbon fibre and steel. Various levels of reinforcement ratio are used for a parametric evaluation. The results indicate that FRP reinforced concrete continuous beams exhibit significantly different response characteristics regarding the moment redistribution and variation of neutral axis depth from those of steel reinforced ones. In addition, it is found that the code recommendations are generally unsafe for calculating the permissible moment redistribution in FRP reinforced concrete beams, but the neglect of redistribution in such beams may be overconservative.     

Influence of internally dropped-off plies on the impact damage of asymmetrically tapered laminated CFRP

This paper presents an experimental study of low velocity impact response of carbon/epoxy asymmetrically tapered laminates. The tests are realised at energy between 10 and 30 J on two types of layup with multiple terminated plies. The type and localisation of damage are analysed using C-scan and micrographs. Then, the data is compared with the response of corresponding respective plain laminate. The effects of some tapering parameters (taper angle, drop-off disposition and configuration) on the impact damage mechanisms are also investigated. Very similar impact damage phenomena are found between tapered and plain laminates. The presence of material discontinuity due to the resin pocket affects less the damage mechanism than the structural difference between the thick and the thin sections.     

Facile synthesis of carbon self-doped g-C3N4 for enhanced photocatalytic hydrogen evolution

Graphite carbon nitride (g-C₃N₄) is an appealing metal-free photocatalyst for hydrogen evolution, but the potential has been limited by its poor visible-light absorption and unsatisfactory separation of photo-induced carriers. Herein, a facile one-pot strategy to fabricate carbon self-doped g-C₃N₄ composite through the calcination of dicyanamide and trace amounts of dimethylformamide is presented. The as-obtained carbon self-doped catalyst is investigated by X-ray photoelectron spectroscopy (XPS), confirming the substitution of carbon atoms in original sites of bridging nitrogen. We demonstrate that the as-prepared materials display remarkably improved visible-light absorption and optimized electronic structure under the premise of principally maintaining the tri-s-triazine based crystal framework and surface properties. Furthermore, the carbon doped g-C₃N₄ composite simultaneously weakens the transportation barrier of charge carriers, suppresses charge recombination and raises the separated efficiency of photoinduced holes and electrons on account of the extension of pi conjugated system. As a result, carbon self-doped g-C₃N₄ exhibits 4.3 times greater photocurrent density and 5.2 times higher hydrogen evolution rate compared with its bulk counterpart under visible light irradiation.